A325 Type 3 Chemical Properties
| Heat Analysis | 120/144ksi, % Comp A | 120/144ksi, % Comp B | 120/144ksi, % Index | 150ksi, % Index |
|---|---|---|---|---|
| Carbon | 0.33 – 0.40 | 0.38 – 0.48 | 0.30 – 0.52 | 0.30 – 0.53 |
| Manganese | 0.90 – 1.20 | 0.70 – 0.90 | 0.60 min | 0.60 min |
| Phosphorus | 0.035 max | 0.035 max | 0.035 max | 0.035 max |
| Sulfur | 0.040 max | 0.040 max | 0.040 max | 0.040 max |
| Silicon | 0.15 – 0.30 | 0.30 – 0.50 | ||
| Copper | 0.25 – 0.45 | 0.20 – 0.40 | 0.20 – 0.60 | 0.20 – 0.60 |
| Nickel | 0.25 – 0.45 | 0.50 – 0.80 | 0.20 min* | 0.20 min* |
| Chromium | 0.45 – 0.65 | 0.50 – 0.80 | 0.20 min | 0.20 min |
| Molybdenum | 0.06 max | 0.10 min* | 0.10 min* | |
| *Either Nickel or Molybdenum must be present in the amount specified*Corrosion Index based on ASTM Guide G101 | ||||